| 6010-
Beater Addition Jointing Sheet |
| Material
Description |
6010
is a comparatively low density, high performance gasket material
designed for elevated temperature applications. It is composed
of a blend of asbestos fibre, inorganic fillers & nitrile
binder. This provides the material with good torque retentions
when combined with a metal core. It's low density makes it ideally
suitable for perforated core applications & the high compressibility
imparts good flange confirmability. This material is available
in light grey, red or green shade.
|
PHYSICAL
PROPERTIES
Density
Compressibility
Recovery
Tensile Strength |
Unit
(gm/cc)
( % )
( % )
(kg/sq.cm) |
Typical Value
1.0
4-0
26
48 |
|
FLUID
IMMERSIONS
WEIGHT INCREASE
A.S.T.M.
Oil 3,5hrs.150° C.
A.S.T.M. Fuel B, 5hrs Room Temp
50% Anti Freeze + 50% Distilled Water 5, hrs, Room Temp.
|
( % )
( % )
( % ) |
49
45
60 |
THICKNESS
INCREASES
A.S.T.M.
Oil 3, 5hrs 150*C.
A.S.T.M. Fuel B, 5hrs Room Temp
50% Anti Freeze + 50% distilled water 5 hrs. Room Temp |
( % ) |
2
4
8 |
SPECIFICATION
COMPLIANCE
A.S.T.M. F104: 127160 E 62 M3. |
TYPICAL
APPLICATIONS
6010 - is a high performance, low density material for use in light
to moderate duty applications. Listed below are few of the applications
where 6010 is intended to be utilized.
EXHAUST MANIFOLD
ENGINE HEAD GASKETS
LIGHT FIXTURES
MAINTENANCE REPAIR OPERATIONS
PIPE FLANGES
LIGHT DUTY TRANSMISSION |
|
|
AVAILABILITY
Roll Width
Roll Size O.D
Roll Weight
Core Size-ID
|
Unit
(MM)
(MM)
(Kg)
(MM) |
Standard
Size
1220
200-225
55-65
75 or 100 |
| 6010
is available in thicknesses 0.5 MM, 0.6, 0.65, 0.7, 0.8, 1.0, 1.2
& 1.5 MM. Other special sizes available on request. |
<<<
| 6030-
Beater Addition Jointing Sheet |
| Material
Description |
6030
is a high performance, medium density gasket material for use
in elevated temperature sealing applications. It is composed of
a blend of inorganic fillers reinforced with asbestos fibres in
a nitrile binder matrix. 6030 offers excellent sealability &
creep relaxation combined with high temperature resistance upto
230°C. This material is available in medium dark grey shade.
|
PHYSICAL
PROPERTIES
Density
Compressibility at 350 kg/sq.cm
Recovery (A.S.T.M. F-36
Tensile Strength (A.S.T.M.F-152)
Density (gm/cc) 12 |
Unit
(gm/cc)
( % )
( % )
(kg/sq.cm) |
Typical Value
12
28
35
80 |
|
FLUID
IMMERSIONS
WEIGHT INCREASE
A.S.T.M. F-146
A.S.T.M.
Oil 3,5 hr, 150° C
A.S.T.M. Fuel B, 5hrs room Temperature ( % ) 32
|
( % )
( % ) |
37
32 |
THICKNESS
INCREASE (A.S.T.M. F-146)
A.S.T.M.
Oil 3, 5hrs 150*C.
A.S.T.M. Fuel B, 5 hrs, Room Temperature
Creep Relaxation, 22 hrs, 100° C. (A.S.T.M F-38 B) |
( % ) |
3
6
22 |
SPECIFICATION
COMPLIANCE
A.S.T.M - F-104 - 125150B4E52M4
6030 is a high performance, medium density gasket material for use
in elevated temperature sealing applications. It is composed of a
blend of inorganic fillers reinforced with asbestos fibres in a nitrile
binder matrix.6030 offers excellent sealability & creep relaxation
combined with high temperature resistance upto 230°C. This material
is available in medium dark grey shade. |
|
|
AVAILABILITY
Roll Width
Roll Size O.D
Roll Weight
Core Size-ID
|
Unit
(MM)
(MM)
(Kg)
(MM) |
Standard
Size
1150
250-275
60-65
75 or 100 |
| 6030
is available in thickness 0.5 MM, 0.55, 0.7, 0.75, 0.8, 0.9, 1.00,
1.2 MM & 1.5MM other special sizes available on request. |
<<<
| 6055-
Beater Addition Jointing Sheet |
| Material
Description |
6055
is a high performance, medium density gasket material for use
in elevated temperature sealing applications. Manufactured from
a blend of asbestos fibre, inorganic fillers & nitrile binder,
it offers excellent sealability at low flange loads & good
resistance to oil, fuels & transmission fluids. This material
is recommended for temperature upto 250°C in heavy duty applications
& is particularly suitable for head gasket where the material
is combined with perforated metal core. This material is available
in dark grey shade.
|
|
PHYSICAL
PROPERTIES
Density
Compressibility at 350 kg/sq.cm (A.S.T.M. F-36)
Recovery (A.S.T.M. F-36)
Tensile Strength (A.S.T.M.F-152)
|
Unit
(gm/cc)
( % )
( % )
(kg/sq.cm) |
Typical Value
1.3
24
40
120 |
|
FLUID
IMMERSIONS
WEIGHT INCREASE ( A.S.T.M. F-146)
A.S.T.M.
Oil 3,5hrs.150° C.
A.S.T.M. Fuel B, 5hrs Room Temp
|
( % )
( % )
( % ) |
35
30
60 |
THICKNESS
INCREASE (A.S.T.M. - F-146)
A.S.T.M.
Oil 3, 5hrs 150°C.
A.S.T.M. Fuel B, 5hrs Room Temp
Creep Relaxation, 22 hrs, 100° C (A.S.T.M. F-38 B) |
( % ) |
4
7
20 |
SPECIFICATION
COMPLIANCE
A.S.T.M. F-104 ; 125150 B 4E52M5
TYPICAL APPLICATIONS
6055 due to it's superlative properties is suitable for a wide range
of applications. Most of these applications utilise 6055 on a perforated
metal core. Compiled below are few of them where 6055 is recommended.
Cylinder Head Gaskets.
Transmission Oil Pan.
Manifold Gaskets.
Engine Oil Pans.
Cylinder Covers.
Gear Boxes. |
|
|
AVAILABILITY
Roll Width
Roll Size
Roll Weight
Core Size I.D
|
Unit
(MM)
(MM)
(Kg)
(MM) |
Standard
Size
1150
250-275
65-70
75 or 100 |
| 6055
is available in thicknesses 0.5 MM, 0.6, 0.7, 0.8, 1.0, 1.2, 1.5MM.
Other special sizes available on request. |
<<<
| 2000
- Non Asbestos Beater Addition Jointing Sheet |
| Material
Description |
2000
is a high performance, low density aramid fibre reinforced gasket
material. It is composed of inorganic fillers combined with mineral
& aramid fibres in nitrile binding matrix. This composition
offers superior performance & reliability in both die cut
& perforated core sealing applications. 2000 is well suited
for head gaskets & other demanding high temperature applications
upto 220°C. This material is available in dark grey colour.
|
PHYSICAL
PROPERTIES
Density
Compressibility at 350 kg/sq.cm (A.S.T.M. F-36)
Recovery (A.S.T.M. F-152)
Tensile Strength (A.S.T.M.F-152)
Loss on ignition at 815°C (A.S.T.M. F-495)
|
Unit
(gm/cc)
( % )
( % )
( % )
( % ) |
Typical Value
1.05
35
22
65/50
30 |
FLUID
IMMERSIONS
WEIGHT
INCREASE (A.S.T.M. F-146)
A.S.T.M.
Oil 3, 5 hrs at 150°C. ( % ) 42
A.S.T.M. Fuel B, 5 hrs at 23°C. ( % ) 38
|
( % )
( % ) |
49
42 |
THICKNESS
INCREASES (A.S.T.M. F-146)
A.S.T.M.
Oil 3 5 hrs at 150°C
A.S.T.M. Fuel B, 5 hrs at 23°C.
Creep Relaxation, 22 hrs at 100°C (A.S.T.M. F-38) |
( % ) |
5
4
22 |
SPECIFICATION
COMPLIANCE
A.S.T.M. F 104: F726160B4E62M3 |
TYPICAL
APPLICATIONS
2000 is a low density high performance aramid fibre gasket material
suitable for wide range of sealing applications at elevated temperatures.
Listed below are applications in which 2000 is utilized.
CYLINDER HEAD GASKET
EXHAUST MANIFOLD
INTAKE MANIFOLD
PETROL ENGINES |
|
|
AVAILABILITY
Roll Width
Roll Size O.D
Roll Weight
Core Size-ID
|
Unit
(MM)
(MM)
(Kg)
(MM) |
Standard
Size
1220
250-275
50-60
75 or 100 |
| 2000
is available in thicknesses 0.5 MM, 0.6, 0.7, 0.8, 0.9 & 1.00
MM. Other special sizes available on request. |
<<<
Asbestos
Products
Asbestos
Mill Board
| 601
- Asbestos Mill Board Jointing Sheet |
| Material
Description |
601
is a stiff & strong asbestos sheet manufactured by wet process
using a blend of selected fibres & nitrile binders. This material
is widely used for copper clad engine gasket, thermal shields
& insulations of electrical devices & home appliances,
various heat & acoustic insulation purposes where temperature
does not exceed 500°C. This material is available in off-white
shade.
|
|
PHYSICAL
PROPERTIES
Density
Compressibility at 70 kg/sq.cm (A.S.T.M. F-36)
Recovery (A.S.T.M F-36)
Tensile Strength (A.S.T.M.F-152)
Loss on ignition at 815°C (A.S.T.M. F-495)
Moisture Content
|
Unit
(gm/cc)
( % )
( % )
(kg/sq.cm)
( % )
( % ) |
Typical Value
1.10
18
28
35
18
2.0 |
FLUID
IMMERSIONS
WEIGHT
INCREASE (A.S.T.M. F-146)
A.S.T.M.
Oil 3, 5 hrs at 150°C. ( % ) 42
A.S.T.M. Fuel B, 5 hrs at 23°C. ( % ) 38
|
( % )
( % ) |
49
42 |
THICKNESS
INCREASES (A.S.T.M. F-146)
A.S.T.M.
Oil 3 5 hrs at 150°C
A.S.T.M. Fuel B, 5 hrs at 23°C.
Creep Relaxation, 22 hrs at 100°C (A.S.T.M. F-38) |
( % ) |
5
4
22 |
SPECIFICATION
COMPLIANCE
A.S.T.M. F 104: F726160B4E62M3 |
TYPICAL
APPLICATIONS
601 is primarily used for insulation where fire ratings are important.
It finds acceptance as a filler for metal composite gasketing in high
heat dynamics such as exhaust manifolds & small stationary engine
cylinder head assemblies. Listed below are few of the applications
where 601 is recommended.
DIESEL ENGINES HEAD GASKETS
Accoustic INSULATION
DOMESTIC APPLICATIONS
EXHAUST MANIFOLD
ELECTRICAL DEVICES
THERMAL SHIELD |
|
|
AVAILABILITY
Roll Width
Roll Weight
Sheet Size (Packed in Crates)
Weight/Crate
|
Unit
(MM)
(kg)
(MM)
(kg) |
Standard
Size
1220
60-65
1200 x 1000
100 |
601
is available in thicknesses 0.5MM, 0.7, 0.75, 0.8 MM in roll form
& 1.0 MM, 1.2, 1.4, 1.5, 1.6, 2.0 MM in sheet form. Other special
sizes available on request.
|
<<<
| 8060
- Non Asbestos Gasket Material |
| Material
Description |
8060 is a high performance medium density
material for use as soft gasket manufactured from a blend of cellulose
& aramid fibres combined with reinforcing inorganic fillers,
imparts an excellent sealing at medium flange loads. It is recommended
as replacement to C A F materials in automotive applications.
|
TEST
SPECIFICATIONS
8060
is primarily used for insulation where fire ratings are important.
It finds acceptance as a filler for metal composite gasketing in high
heat dynamics such as exhaust manifolds & small stationary engine
cylinder head assemblies. Listed below are few of the applications
where 8060
is recommended.
DIESEL ENGINES HEAD GASKETS
Accoustic INSULATION
DOMESTIC APPLICATIONS
EXHAUST MANIFOLD
ELECTRICAL DEVICES
THERMAL SHIELD |
|
|
TEST
SPECIFICATIONS
PHYSICAL
PROPERTIES
1.
Thickness Range
2. Density
3. Compressibility at 100 psi
4. Recovery
5. Tensile Strength
6. A.S.T.M. Oil 3 (5 Litres at 150°C.)
Weight Increase
Thickness Increase
7. A.S.T.M. Fuel 3 (5 Litres at R.T.)
|
Unit
mm
gm/cc
%
%
Kg/Cm2
%
%
|
Specifications
0.4-1.5
1.2-1.3
10-20
40 Min
120 Min
25-40
25 Max
25-40
25 Max
|
<<<
Asbestos
Products
Non
Asbestos Mill Board
| Non
Asbestos Fiber Gasket Jointing Sheets |
| Material
Description |
This
material is made with carefully selected blend of synthetic Aramid
fibre with a high quality elastomer.The various elastomers used
are NBR, SBR.
|
|
APPLICATION
Non Asbestos Range
A.M.
37
Oil resistant Gasket Material for light to medium loadings
A.M. 30
Oil resistant Gasket material for medium to higher
loadings, good resistance to water, gases, oils and
fuels.
A.M. 32
High performance, oil resistant Gasket material with
excellent thermal, chemical and mechanical
properties.
A.M. 33
Gasket material with controlled swell properties in oil,
wide range of application in automotive and
chemical industry.
|
TECHNICAL
DATA SHEET
COMPRESSED NON-ASBESTOS MATERIAL
PROPERTIES
|
A.M.
NAM 37
|
A.M
NAM 30
|
A.M.
NAM 32
|
A.M
NAM 33
|
DENSITY
|
1.7-2.0
|
1.7-2.0
|
1.7-2.0
|
1.7-2.0
|
| TENSILE
STRENGTH |
|
|
|
|
(N
/ MM) ASTM F153(N/MM) DIN 52910
|
7
5 |
10
7 |
14
11 |
12
9 |
| STRESS
RESISTANCE |
|
|
|
|
(N
/ MM2) DIN52913 16hr, 300 C
(N / MM2) DIN52913 16hr, 175 C
|
20
28 |
20
30 |
25
36 |
20
30 |
| COMPRESSIBILITY
% |
7-15 |
7-15
|
6-12
|
6-12
|
| RECOVERY
% |
³50
|
³50
|
³50
|
³50
|
| FLUID
RESISTANCE ASTM Oil No. 3 |
|
|
|
|
Mass
Increase
Thickness Increase |
£15
£10 |
£10
£10 |
£10
£8 |
£10-30
£10-30 |
| FUEL
B |
|
|
|
|
Mass
Increase
Thickness Increase |
£10
£10 |
£10
£10 |
£10
£7 |
£10-30
£10-30 |
| Swelling
in Water/antifreeze 50:50 (5h 1000C) |
|
|
|
|
Mass
Increase
Thickness Increase |
£5
£15 |
£5
£15 |
£5
£15 |
-
- |
| IGNITION
LOSS % DIN 52911 |
£28
|
£36
|
£30
|
£35
|
SEALIBILITY
(CM3/Min)
DIN 3535 PART GFA |
£1.0
|
£1.0
|
£0.5
|
£1.0
|
MAXIMUM
OPERATING
TEMPERATURE (deg c) |
250 |
250 |
250 |
250 |
MAXIMUM
PEAK
TEMPERATURE (deg c) |
400 |
400 |
400 |
400 |
| MAXIMUM
OPERATING TEMPERATURE (bar) |
|
100 |
100 |
100 |
|
<<<
Cellulose
Paper
| Cellulose
Based Gasket Paper |
| Material
Description |
Cellulose
paper is a high density cellulose based gasket material for automotive
& industrial applications. It is composed of cellulose fibres
& nitrile rubber binders manufactured by beater addition process.
It's medium compressibility & high torque retention properties
elevate it to heavy duty applications where resistance to crushing
& extrusion are required better dimensional stability &
good resistance to oil, fuel & water give it a clear advantage
over impregnated cellulose products. It is suitable upto 170°
C.
|
PHYSICAL
PROPERTIES
Density
Compressibility at 70kg/sq.cm (A.S.T.M. F-36)
Recovery (A.S.T.M. F-36)
Tensile Strength (A.S.T.M.F-152) |
Unit
(gm/cc)
( % )
( % )
( % ) |
Typical Value
1.0
17
45
150 |
FLUID
IMMERSIONS
WEIGHT
INCREASE (A.S.T.M. F-146)
A.S.T.M.
Oil 3, 22 hrs at 21°C.-29°C ( % ) 42
A.S.T.M. Fuel B, 22 hrs at 21°C - 29°C. ( % ) 40 |
( % )
( % ) |
49
42 |
THICKNESS
INCREASES (A.S.T.M. F-146)
A.S.T.M.
Oil 3, 22 hrs at 21°C - 29°C. ( % ) 6
A.S.T.M. Fuel B, 22 hrs at 21°C-29°C. ( % ) 7 |
(
% ) |
6
7 |
|
DISTILLED
WATER(A.S.T.M.
F-146)
Weight
Increase, 22 hrs at 21°C-29°C.
Thickness Increase, 22 hrs at 21°C-29°C.
|
(
% )
(
% ) |
57
28 |
SPECIFICATION
COMPLIANCE
A.S.T.M. F-104-88 ; 334156E52M6 |
TYPICAL
APPLICATIONS
Cellulose paper is a high density cellulose Gasket material suitable
for use in many sealing applications. Listed below are applications
where Cellulose paper is utilized.
ANY TYPE OF SEALING APPLICATIONS
MATERIAL HANDLING EQUIPMENTS
CHEMICAL PUMPS & PIPE LINES DIESEL ENGINES
OIL / FUEL PUMPS
CARBURETORS
WATER PUMP
GEAR BOXES
OIL PANS
|
|
|
AVAILABILITY
Roll Width
Sheet Size (Packed in crates)
Roll Weight
Core Size-ID
Weight / Roll (kg) 50-55
Weight / Crate (kg) 95-100
|
Unit
(MM)
(MM)
(Kg)
(MM)
(Kg)
(Kg) |
Standard
Size
1200
1200-1000
50-60
75
50-55
95-100 |
| Cellulose
paper is available in thicknesses - 0.25 MM, 0.40, 0.50, 0.75, 0.80
MM in roll form & 1.0 MM, 1.2 & 1.5 MM in sheet form. Other
special sizes available on request. |
<<<